| Mudell | Residwu tal-Għarbel | Volatili | Densità apparenti | Viskożità Intrinsika | Nota | |
| Universali | DL-125 | ≤2.0 | ≤1.5 | 0.55±0.10 | 5.0-6.0 | DOWK-125 korrispondenti |
| DL-120N | ≤2.0 | ≤1.5 | 0.45±0.10 | 3.0-4.0 | DOWK-120N korrispondenti | |
| DL-128 | ≤2.0 | ≤1.5 | 0.55±0.10 | 5.2-5.8 | LG PA-828 korrispondenti | |
| DL-129 | ≤2.0 | ≤1.5 | 0.45±0.10 | 3.0-4.0 | LG PA-910 korrispondenti | |
| Lubrikazzjoni | DL-101 | ≤2.0 | ≤1.5 | 0.50±0.10 | 0.5-1.5 | Korrispondenti DOWK-175 & KANEKA PA-101 |
| DL101P | ≤2.0 | ≤1.5 | 0.50±0.10 | 0.6-0.9 | Korrispondenti DOWK-175P & ARKEMA P-770 | |
| Trasparenza | DL-20 | ≤2.0 | ≤1.5 | 0.40±0.10 | 3.0-4.0 | Korrispondenti KANEKA PA-20 & DOWK-120ND |
| Tip SAN | DL-801 | ≤2.0 | ≤1.5 | 0.40±0.05 | 11.5-12.5 | |
| DL-869 | ≤2.0 | ≤1.5 | 0.40±0.05 | 10.5-11.5 | CHEMTURA BLENDEX korrispondenti 869 | |
| Speċjali | DL-628 | ≤2.0 | ≤1.5 | 0.45±0.05 | 10.5-12.0 | |
| DL-638 | ≤2.0 | ≤1.5 | 0.45±0.05 | 11.0-12.5 | ||
Karatteristiċi tal-Prestazzjoni:
Acrylic Processing Aids Series hija kopolimeru akriliku żviluppat mill-kumpanija tagħna għall-promozzjoni tal-plastifikazzjoni tal-materja prima tal-PVC. Jista 'jikseb plastifikazzjoni tajba f'temperatura baxxa tal-iffurmar u jtejjeb il-proprjetajiet mekkaniċi tal-prodotti tal-PVC lesti u t-tleqqija tal-wiċċ.
Ippakkjar u Ħażna:
Borża tal-karta komposta: 25kg/borża, miżmuma taħt is-siġill f'post niexef u dellija.